Zhengzhou BBN steel company was established in 2000. After more than ten years of development, it has formed a professional operation pattern integrating R&D, production, sales and after-sales service. In recent years, A573 grade 70 CS steel carbon plate based on a high starting point and high technology, the company has vigorously developed various steel products A573 grade 70 CS steel carbon plate and deep-processed parts, steel structures, precision castings, seamless pipes.
Product : 35SiMn alloy structural steel Standard: GB/T 3077-2015 Heat treatment Quenching temperature/℃ First quenching 900 Second quenching - Coolant water tempering temperature/℃ 570 Coolant water.oil Sample size: sample blank size/mm: 25
Weather-resistant steel plate refers to steel plate that is resistant to weathering and corrosion. A573 grade 70 CS steel carbon plate, Weather-resistant steel plate can adapt well to the environment and is widely used in construction, bridges, roads and other fields with outstanding performance characteristics. One of the outstanding advantages of weather-resistant steel plate is its ability to adapt to a variety of different environments, whether it is in severe cold areas or tropical areas. The weather-resistant steel plate can better maintain its characteristics in various complex environment.
The effect of nitrogen on steel performance is similar to that of carbon and phosphorus. With the increase of A573 grade 70 CS steel carbon plate nitrogen content, the strength of steel can be improved, plasticity especially toughness can be significantly reduced, weldability becomes worse, and cold brittleness is intensified. Nitrogen with aluminum, niobium, vanadium and other elements can reduce its adverse effects, improve the performance of A573 grade 70 CS steel carbon plate steel, can be used as an alloying element of low alloy steel.
As per JIS G3101 standard, the Carbon (C), Silicon (Si) and Manganese (Mn) content of SS400 steel plate are not controlled. Phosphorus (P) content of A573 grade 70 CS steel carbon plate, JIS SS400 steel plate is 0.050% Max and Sulphur (S) content is 0.050% Max. The SS400 steel melting point is 1430 Degree Celsius, Brinell Hardness is 160HB, density is 7.85g/cm3, Young’s Modulus is 190-210Gpa. The strength and elongation of JIS SS400 steel plate varies with thickness. Generally, the tensile strength of SS400 steel plate is 400-510 Mpa. Elongation is above 21%. Yield strength ≥245Mpa for thickness≤16mm. When the JIS SS400 steel plate is thciker than 100mm, the yield strength shall not less than 205Mpa.
Our company stocks a wide range of hot rolled carbon steel plate distributed globally from our service centers in the U.S., Canada, Mexico, U.K, France, Shanghai, and Singapore. Customers calling for A573 grade 70 CS steel carbon plate A516 a lot of times are also trying to get their arms around forecast issues. As our customers continue to work on their forecasts, IRON & Steel has options to help you conduct structured forecast reviews and put inventory strategies in place to effectively manage any impact from forecast variability.
The 365 day service system is implemented, and the business, loading and delivery are handled as usual in holidays and festivals. Actively help users solve difficulties. When users encounter difficulties in handling business, they should actively coordinate with the external solution; if they need to solve the problems internally, they should solve them in a timely manner without prevarication and wrangling. In line with the A573 grade 70 CS steel carbon plate principle of "fairness, justice and timeliness", coordinate with relevant departments and deal with all kinds of objections in a timely manner.