The company was established in 2000, covering an area of more than 4,500 acres. It has fixed assets of 200 million yuan, and employs more than 1,200 people. It has now formed coking, sintering, white ash, pellets, ironmaking, A588 Gr A heavy plate steelmaking, steel rolling, oxygen production, gas and waste heat The complete circular economy industrial chain including power generation, comprehensive utilization of slag, soot and dust treatment, sewage treatment and recycling, etc. It mainly produces hot-rolled steel plates and A588 Gr A heavy plate carbon structural steels, high-quality carbon structural steels, low-alloy high-strength steels, medium and wide-band steels for cold-rolled stamping, and hot-rolled coils.
A633Gr.C,D steel plate A537CL1/A633Gr.C,D steel plate, under ASTM-SAE standard A537CL1/A633Gr.C,D steel plate, under ASTM-SAE standard, we can regard A588 Gr A heavy plate, A537CL1/A633Gr.C,D steel plate as Fine-grain structural steels, normalised rolled steel. A537CL1 steel plate is one mainly of Fine-grain structural steels, normalised rolled steel,A537CL1/A633Gr.C,D steel plate is under ASTM-SAE standard equivalent to DIN:TStE355, EN:S355NL, which with a minimum impact energy of 20J at temperatures not lower than -20 degree and the tensile strength of A537CL1/A633Gr.C,D is 4800 to 620 MPa.
Q345B material is a low carbon alloy steel grade with good overall performance, low temperature performance, cold stamping performance, welding performance and machinability. Q345 serues steel is widely used in bridges, vehicles, ships, buildings, pressure vessels. Q represents the yield of this material, and the number 345 refers to the yield value of this material, which is around 345MPa. As the thickness of the material increases, its yield value decreases.
In the second step of hot rolling process, different finished mills are used to roll billets or continuous casting billets into finished steel of proper shape and size. This A588 Gr A heavy plate production process is called finished product production, which is generally divided into two stages of rough rolling and finish rolling. In the roughing stage, a large amount of reduction (reduction per pass) is adopted to reduce the number of passes and improve the output; after roughing, the finishing stage is entered, and the finishing is carried out with a small amount of reduction to achieve a good surface and accurate A588 Gr A heavy plate size.
A588 Gr A heavy plate, 09CuPCrNi-A weather resistant steel is origined in China. Its equivalent grades are JIS SPA-H, BS WR50A, Corten steel, etc. The Cu, P, Cr, Ni are important elements that gave 09CuPCrNi-A weather resistant steel its weathering ability. The Cu content of 09CuPCrNi-A steel is 0.25–0.50, P content is 0.060-0.12, Cr content is 0.30-1.25, Ni content is 0.12-0.65. For 09CuPCrNi-A steel coil ≤ 4mm, the min. yield strength is 310Mpa, min. tensile strength 440Mpa. For 09CuPCrNi-A steel sheets >4mm, the min. yield strength is 345Mpa, min. tensile strength 480Mpa.
The after-sales service department will pay return visit to each customer by call or email, report problems found during the return visit in time, and discuss with the production and quality inspection center to propose effective solutions and follow up in a timely manner, so as to ensure the benefits each customer are fully guaranteed, and to provide customers with more value-added services.