A283 grade D CS steel carbon plate, C45 (1.0503) is a kind of medium carbon high quality steel with high strength. Because of its poor hardenability, it is generally used in normalized state. When the mechanical properties are required to be high, C45 steel needs to be quenched and tempered. Its cold deformation plasticity is medium, and its cutting workability in annealing and normalizing state is better than that of quenched and tempered state. C45 is the name in the DIN standard. It is called 45# steel in the Chinese standard, S45C in the JIS standard, and AISI 1045 in the ASTM standard.
In February, the European steel price index was 161.2 points, up 1.3 points on a month on month basis, up 0.8%; the euro zone manufacturing PMI was 49.2%, up 1.3 percentage points on a month on month basis. The manufacturing PMI of Germany, Italy, France and Spain were 48%, 48.7%, 49.8% and 50.4% respectively. This month, among the main steel products such as A283 grade D CS steel carbon plate in the German market, the price of wire rod decreased slightly, the price of section steel remained stable, and other products continued to rise.
Structural steel plate A283 grade D CS steel carbon plate discount online 15*2320*9790, 12.5*2060*7410, 12*1540*5390, 12.5*1730*14930, 11*3910*6450, 17*2000*10650, 13.5*1905*8920, 6*1730*7840, 12.5*3790*8900, 12.5*3600*8810, 32*1301*6600, 12.5*1530*8000, 12*1590*9770, 16*2300*14200, 14.5*3690*10960, 20*2100*8950, 6*1800*4500, 14*1700*9200, 12.5*1790*15910, 5*1829*6096, 13*3200*10700, 9*1301*4000, 11*1510*5370, 12.5*1730*14770, 12.7*1829*6096, 13*2970*9800, 13.5*2890*5350, 12.5*2145*10360, 14*1860*13880, 24*2715*7800.
Preheating cutting: The most effective way to prevent steel plate cutting cracks is to preheat before cutting. Before flame cutting, the steel plate is usually preheated, and the preheating temperature mainly depends on the quality level and thickness of the steel plate. The preheating method can be carried out with flame burner, electronic heating pad, or heating furnace. In order to determine the preheating effect of the steel plate, the required temperature should be tested at the heating point.