BBN STEEL supply various size of plate product A514 grade E quenched and tempered steel Size stock: 16*1555*11400, 12.7*3316*10500, 12.7*2438.4*12192, 23*2330*11300, 12.7*2518*11380, 6.5*2450*12500, 18*1860*12000, 12.7*2515*12000, 9*2440*12500, 15.1*1550*10400, 12*2680*12000, 12*2520*12000, 18*2020*12000, 11*2365*12000, 14*3470*12000, 12.7*2518*11380, 18*1700*12000, 9.2*2530*12000, 12*2680*12000, 68*2350*7500.
The company mainly supply mild A514 grade E quenched and tempered steel steel plate, alloy steel plate, boiler plate, corten steel plates for railway, marine, automotive, home appliances, shipbuilding, construction, machinery manufacturing and oil tank projects. While accelerating the development of the main steel industry, the company adheres to a diversified development strategy and actively develops the other industry like household products, face mask machine, precision casting producing, steel structures, and heavy plates processing service.
There is an inherent difference between the cold forming properties of low-alloy high-strength steel and carbon structural steel. First of all, a certain amount of permanent deformation of low-alloy high-strength steel requires greater force than A514 grade E quenched and tempered steel, carbon structural steel of the same size. Second, when low-alloy high-strength steel is formed, a slightly larger allowable amount for springback should be given. According to experience, unless the low-alloy high-strength steel is processed to control the shape of inclusions, it is necessary to use a larger bending radius than carbon structural steel during cold forming.
The A514 grade E quenched and tempered steel processing performance is good. Due to the uniform control of steel plate performance, excellent performance coordination and good toughness guarantee, the steel plate bending processing, drilling, cutting and other mechanical processing properties are excellent. In addition, the surface of the A514 grade E quenched and tempered steel steel plate is smooth and beautiful by inhibiting and removing oxide scale from slab heating to rolling process and heat treatment in furnace without oxidation atmosphere.