A514 grade C high yield strength steel plate chemical composition (melting analysis)%C: 0.02-0.20, Si: 0.15-0.30, Mn: 1.10-1.50, P max.: 0.035, S max.: 0.035, B max.: 0.005, Mo: 0.15-0.30The mechanical properties in thickness (mm) T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18
The production process of hot-rolled steel plate and cold-rolled steel plate is different. Hot rolled steel plate is rolled at high temperature, and cold rolled steel plate is rolled at normal temperature. Generally speaking, cold rolled steel plate has better strength and hot rolled steel plate has better ductility. The thickness of A588 grade B high strength steel cold rolling is generally smaller, and that of hot rolling can be larger. The surface quality, appearance and dimension accuracy of cold rolled steel plate are better than that of hot rolled steel plate.
First of all, we should establish a correct concept of after-sales service. Service concept is an important part of corporate culture and a long-term enterprise value concept. Our company's after-sales service embodies the concept of "customer first, sincere service for customers". As long as we are in the "sincere service for users" under the guidance of the idea, I believe we will get rich returns.