Focusing on the energy conservation and emission reduction objectives proposed by the municipal government, the company gives full play to the advantages of A588 grade A heavy plate circular economy formed after the comprehensive completion and operation, and vigorously promotes the implementation of energy conservation objectives. Through measures such as energy saving, technological innovation and A588 grade A heavy plate management strengthening, the energy saving target of annual reduction of added value energy consumption by 7%. It has made great contribution to energy saving of over completion.
Medium thick steel plate refers to the steel plate with a thickness of not less than 3 mm but less than 20 mm. It can be produced by reversible hot rolling medium and heavy plate mill, and its thin products can also be processed by cold rolling mill. A588 grade A heavy plate, Medium thick steel plates are mainly used in boilers, shipbuilding, railway cars, automobiles, containers, military industry, national defense, construction, bridges and containers.
16MnDR steel plate is suitable for low temperature pressure vessels manufacturing. Grade 16Mn- indicates that the content of manganese (Mn) in the steel plate is relatively high, about 1% -1.6%, D- indicates low temperature, R- indicates pressure vessel. (Normally, when the content of a certain chemical element in steel is high, it needs to be marked in the material, for example, 1.6% manganese is written as 16Mn; certain elements such as Cr and Mo are higher, written as Cr1, Mo1, Such as 12Cr2Mo1R.) The normal delivery status is normalized delivery (Normalized).
S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the A588 grade A heavy plate rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of A588 grade A heavy plate steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.
High strength steel A588 grade A heavy plate product selling stock:8*2000*6000, 12*1524*6096, 16*1720*10070, 12*2335*5000, 8*2000*9300, 15*2430*5650, 20*1830*10950, 14*1524*6096,8*2000*5300, 15*2000*12000, 22*2438*6096, 15*2000*10000, 10*1600*6500, 14*2000*10000, 22*2150*8500,18*2000*10000, 10*1600*6500, 14*2438*6096, 38*2700*6000, 40*2030*12400.
If customers have any difficult problems during use of the steel materials, they can contact the company's after-sales service department to feedback the existing problems. The after-sales department will reply as soon as possible to ensure that each customer has a good after-sales experience. Under special circumstances, the after-sales service department will start the problem-solving process, and the engineers in charge of the area will quickly follow up to solve the problem.