"SA572 grade 55 [380] steel chemical composition(%)Carbon max.: 0.26Manganese max.: 1.35Phosphorus Max.: 0.030Sulfur Max.: 0.030Silicon max.: 0.40A572 grade 65 high strength steel, SA572 Grade 55 [380] steel mechanical propertiesTensile strength min. MPa: 380Yield strength min. MPa: 485Elongation % min. in 200mm : 17Elongation % min. in 50mm : 20"
The steel such as A572 grade 65 high strength steel delivered in the hot-rolled state has a certain degree of corrosion resistance due to the high temperature, so it can be stored in the open air. However, this layer of oxide scale also makes the hot-rolled steel surface rough and the size fluctuates greatly. Therefore, the steel with smooth surface, accurate size and good mechanical properties is required to be produced by using hot-rolled semi-finished products or finished products as raw materials and then cold rolling.
The advantage of plasma cutting is that it can cut thin plates, stainless steel and non-ferrous metals, and the cutting speed is fast. The disadvantage of plasma cutting is that the incision will have a slope, and there will be noise when cutting. The advantages of water jet cutting are wide cutting range and environmental protection, but the disadvantages of water jet cutting are slow cutting speed and high energy consumption. Do you know what is the best cutting method for A572 grade 65 high strength steel?
The carbon content of A572 grade 65 high strength steel, hot rolled steel plate is slightly higher than that of cold rolled steel plate. Hot rolled steel plate has low hardness, easy processing and good ductility. Cold rolled steel plate has high hardness and is difficult to process, but it is not easy to deform and has high strength. The strength of hot-rolled steel plate is relatively low, the surface quality (oxidation finish) is low, but the plasticity is good, and it is generally medium thick plate.