At the same time of doing well in A514 grade Q structural steel material production and operation, Yunnan company focused on completing the four phases of technical transformation construction projects, realizing industrial upgrading, improving equipment level, and laying a good foundation for the future development of the company. In the A514 grade Q structural steel material technological transformation project, pollution control facilities have been built synchronously, and a large number of comprehensive utilization projects, such as comprehensive sewage treatment and recycling project, blast furnace gas waste heat and residual pressure power generation, have been invested and constructed.
BBN company has implemented a resource strategy combining global resource procurement, domestic resource unified purchase, and joint purchase and distribution. It has maintained good relations of cooperation with more than 100 domestic and foreign steel mills, and can purchase low-quality and high-quality steel futures in all directions and through multiple channels. The company can grasp the specifications and quantities of the spot resources of major steel mills in real time, and can timely and quickly meet customer demand for steel spot resources.
Preheating cutting: The most effective way to prevent steel plate cutting cracks is to preheat before cutting. Before flame cutting, the steel plate is usually preheated, and the preheating temperature mainly depends on the quality level and thickness of the steel plate. The preheating method can be carried out with flame burner, electronic heating pad, or heating furnace. In order to determine the preheating effect of the steel plate, the required temperature should be tested at the heating point.
In January, 2019, our South Africa customer purchased 669 tons S235J2+N carbon steel plates to use in their tank fabrication project . S235J2 steel, as a non-alloy structural steel grade, is mainly used in structural projects and tanks. J2 symbol -20 temperature impact test. The client required CEV 0.38%, S≤0.01%, 100% UT, Charpy V-notch impact test at-20℃, Z25 for S235J2+N plates. After they receiving the S235J2+N steel plates, the customer are very satisfied with the quality of this batch of A514 grade Q structural steel material products.
A514 grade Q structural steel material, S235JR VS S275JR VS S355JR plates in yield strength: For plate thickness ≤16mm, the min. yield strength of S235JR plates is 235 Mpa, S275JR plates is 275 Mpa, S355JR plates is 355 Mpa. The yield strength of S235JR S275JR S355JR plates reduces with the increasing of plate thickness. S235JR VS S275JR VS S355JR plates in tensile strength: For plate thickness 3-100mm, the tensile strength of S235JR plates is 360-510 Mpa, S275JR plates is 410-560 Mpa, S355JR plates is 470-630 Mpa. For plate thickness 100-150mm, the tensile strength of S235JR plates is 350-500 Mpa, S275JR plates is 400-540 Mpa, S355JR plates is 450-600 Mpa.
Company through its own A514 grade Q structural steel material website, multimedia, radio, newspapers, the group, the handbook of the corporate culture carrier, approved and publicity column, in-depth to carry out enterprise culture construction, also through photography, painting, calligraphy, cartoon, speech, and the songs of the enterprise design, various cultural and sports activities to carry out enterprise culture construction.